ASTM A333 Grade 6 Low Temperature Carbon Steel Pipes

Product Description

We are supplying a comprehensive range of ASTM A333 Grade 6 Low Temperature Carbon Steel Pipes for the right technical solution. Hallmark Metallica manufacture & export wide selections of ASTM A333 Grade 6 Low Temperature Carbon Steel Pipes ASTM A106 Grade A ASTM A106 Grade B ASTM A106 Grade C at most attractive price as per customer requirements, we can also manufacture ASTM A333 Grade 6 Low Temperature Carbon Steel Pipes in ASTM/ASME/ANSI grades as per our customer budget, we enjoy the reputation supplying ASTM A333 Grade 6 Low Temperature Carbon Steel Pipes at cheapest in steel industries around the globe.

Grade 1 Grade 3 Grade 6
psi MPa psi MPa psi MPa
Tensile Strength, min 55,000 380 65,000 450 60,000 415
Yield Strength, min 30,000 205 35,000 240 35,000 240
Longitudinal  Transverse Longitudinal  Transverse Longitudinal  Transverse
Elongation in 2 in. or 50 mm, (or 4D), min, %:
Basic minimum elongation for walls 5/16 in. [8 mm] and over in thickness, strip tests, and for all small sizes tested in full section 35 35 30 20 30 16.5
When the standard round 2-in. or 50-mm gage length or proportionally smaller size test specimen with the gage length equal to 4D (4 times the diameter) is used 28 20 22 14 22 12
For strip tests, a deduction for each 1/32in. [0.8 mm] decrease in wall thickness below 5/16 in. [8 mm] from the basic minimum elongation of the following percentage 1.75 1.25 1.50 1.00 1.50 1.00
  Elongation in 2 in. or 50 mm, min, %:
welded pipe with wall thicknesses of 0.120 in. [3 mm] and larger, shall not be less than the values prescribed:
Size of Specimen, min Minimum Average Notched Bar Impact Value of Each Set of Three Specimens Minimum Notched Bar Impact Value of One Specimen Only of a Set Impact Temperature
  ft-lbf J ft-lbf J Grade Min Impact 
Test Temp
10 by 10 13 18 10 14   F C
10 by 7.5 10 14 8 11 1 -50 -45
10 by 6.67 9 12 7 9 3 -150 -100
10 by 5 7 9 5 7 6 -50 -45
10 by 3.33 5 7 3 4  
10 by 2.5 4 5 3 4  
  Composition, %  
Element Grade 1 Grade 3 Grade 6
Carbon, max 0.30 0.19 0.30
Manganese 0.40 - 1.06 0.31 - 0.64 0.29 - 1.06
Phosphorous, max 0.025 0.025 0.025
Sulfur, max 0.025 0.025 0.025
Silicon 0.18 -0.37 0.10 min
Nickel 3.18 - 3.82

For each reduction of 0.01% carbon below 0.30%, an increase of 0.05% manganese above 1.06% would be permitted to a maximum of 1.35% manganese.

When Grade 6 is ordered under this specification, supplying an alloy grade that specifically requires the addition of any element other than those listed for the ordered grade is not permitted. However, the addition of elements required for the deoxidation of the steel is permitted.

Transverse or Longitudinal Tension Test and Flattening Test, Hardness Test, or Bend Test
For material heat treated in a batch-type furnace, tests shall be made on 5% of the pipe from each treated lot. For small lots, at least one pipe shall be tested.

For material heat treated by the continuous process, tests shall be made on a sufficient number of pipes to constitute 5% of the lot, but in no case less than 2 pipe.

Hydrostatic Test
Impact Test -  One notched bar impact test, consisting of breaking three specimens shall be made from each heat represented in a heat-treatment load on specimens taken from the finished pipe.