Stainless Steel 316l Pipes Tubes | Hallmark Metallica is one of the reputed exporters of Stainless Steel 316l Pipes Tubes

 


Type 316L is the low carbon version of 316 stainless. With the addition of molybdenum, the steel is popular for use in severe corrosion environments due to the materials immunity from boundary carbide precipitation (sensitisation). The material is widely used in heavy gauge welded components and weld annealing is only required where the material is for use in high stress environments. 316L has an extensive variety of uses especially in marine applications due to the materials high corrosion resistance.

Benefits of using Type 316L Stainless Steel
  • Low carbon content eliminates carbon precipitation in the welding process
  • Can be used in severe corrosive environments
  • Improved anti-corrosion scope due to added Molybdenum
  • Weld annealing only required in high stress applications
  • Very similar to Grade 316 in chemical composition and mechanical properties

316 & 316L steel plate and pipes have common properties and are often stocked with Dual Certification, where it is determined that both have properties and composition which comply with both steel types. 

Type 316H is excluded from this scenario by virtue of the fact that unlike 316 & 316L, 316H is engineered to work in elevated working temperatures. 

Product Range

Specifications
: ASTM A269 / ASTM A312

Sizes (Seamless):
1/2" NB - 24" NB

Sizes (ERW):
1/2" NB - 24" NB

Sizes (EFW):
6" NB - 100" NB  

Wall Thickness available:
Schedule 5S - Schedule XXS (heavier on request)

Other Materials Testing:

NACE MR0175, H2 SERVICE, OXYGEN SERVICE, CRYO SERVICE, etc.

Dimensions:

All Pipes is manufactured and inspected/tested to the relevant standards including ASTM A269 / ASTM A312


Background of 316L

Grade 316 is the standard molybdenum-bearing grade, second in importance to 304 amongst the austenitic stainless steels. The molybdenum gives 316 better overall corrosion resistant properties than Grade 304, particularly higher resistance to pitting and crevice corrosion in chloride environments. It has excellent forming and welding characteristics. It is readily brake or roll formed into a variety of parts for applications in the industrial, architectural, and transportation fields. Grade 316 also has outstanding welding characteristics. Post-weld annealing is not required when welding thin sections.

Grade 316L, the low carbon version of 316 and is immune from sensitisation (grain boundary carbide precipitation). Thus it is extensively used in heavy gauge welded components (over about 6mm). Grade 316H, with its higher carbon content has application at elevated temperatures, as does stabilised grade 316Ti.


The austenitic structure also gives these grades excellent toughness, even down to cryogenic temperatures.


Composition of 316L


Table 1.
 Composition ranges for 316 grade of stainless steels.

Grade
 
C
Mn
Si
P
S
Cr
Mo
Ni
N
316
Min
-
-
-
0
-
16.0
2.00
10.0
-
Max
0.08
2.0
0.75
0.045
0.03
18.0
3.00
14.0
0.10
316L
Min
-
-
-
-
-
16.0
2.00
10.0
-
Max
0.03
2.0
0.75
0.045
0.03
18.0
3.00
14.0
0.10
316H
Min
0.04
0.04
0
-
-
16.0
2.00
10.0
-
max
0.10
0.10
0.75
0.045
0.03
18.0
3.00
14.0
-

Mechanical Properties

Table 2. Mechanical properties of 316 grade stainless steels.

Grade
Tensile Str
(MPa) min
Yield Str
0.2% Proof
(MPa) min
Elong
(% in 50mm) min
Hardness
Rockwell B (HR B) max
Brinell (HB) max
316
515
205
40
95
217
316L
485
170
40
95
217
316H
515
205
40
95
217

Note: 316H also has a requirement for a grain size of ASTM no. 7 or coarser.

Physical Properties

Table 3. Typical physical properties for 316 grade stainless steels.

Grade
Density
(kg/m3)
Elastic Modulus
(GPa)
Mean Co-eff of Thermal Expansion (m/m/0C)
Thermal Conductivity
(W/m.K)
Specific Heat 0-1000C
(J/kg.K)
Elec Resistivity
(nΩ.m)
0-1000C
0-3150C
0-5380C
At 1000C
At 5000C
316/L/H
8000
193
15.9
16.2
17.5
16.3
21.5
500
740


Grade Specification Comparison of 316L

Table 4. Grade specifications for 316 grade stainless steels.

Grade
UNS
No
Old British
Euronorm
Swedish
SS
Japanese
JIS
BS
En
No
Name
316
S31600
316S31
58H, 58J
1.4401
X5CrNiMo17-12-2
2347
SUS 316
316L
S31603
316S11
-
1.4404
X2CrNiMo17-12-2
2348
SUS 316L
316H
S31609
316S51
-
-
-
-
-

Note: These comparisons are approximate only. The list is intended as a comparison of functionally similar materials not as a schedule of contractual equivalents. If exact equivalents are needed original specifications must be consulted.

Corrosion Resistance of 316L Stainless Steel Pipes and Tubes

Excellent in a range of atmospheric environments and many corrosive media - generally more resistant than 304. Subject to pitting and crevice corrosion in warm chloride environments, and to stress corrosion cracking above about 600C. Considered resistant to potable water with up to about 1000mg/L chlorides at ambient temperatures, reducing to about 500mg/L at 600C.

316 is usually regarded as the standard “marine grade stainless steel", but it is not resistant to warm sea water. In many marine environments 316 does exhibit surface corrosion, usually visible as brown staining. This is particularly associated with crevices and rough surface finish.

Heat Treatment of 316L Stainless Steel Pipes and Tubes

Solution Treatment (Annealing) - Heat to 1010-11200C and cool rapidly. These grades cannot be hardened by thermal treatment.